Characteristics for grade     MNZHKT5-1-0.2-0.2   ( МНЖКТ5-1-0.2-0.2 )



      Grade :     MNZHKT5-1-0.2-0.2   ( МНЖКТ5-1-0.2-0.2 )
      Classification :   Copper-nickel alloys
      Equivalent grades:     Is absent



Chemical composition in % for grade   MNZHKT5-1-0.2-0.2   ( МНЖКТ5-1-0.2-0.2 )
Ni+Co Fe C Si Mn Ti Cu PbZn Impurity
5 - 6.51 - 1.4max   0.030.15 - 0.30.3 - 0.80.1 - 0.390 - 93.45max   0.005max   0.5 all 0.7
Comment: Cu is a basis; the percentage of Cu is given approximately.


Mechanical properties under Т=20oС for grade   MNZHKT5-1-0.2-0.2   ( МНЖКТ5-1-0.2-0.2 )
Assortment Dimension Direct. sв sT d5 y KCU Heat treatment
- mm - MPa MPa % % kJ / m2 -
Wire, GOST 16130 - 90     440        



Types of delivery of grade   MNZHKT5-1-0.2-0.2   ( МНЖКТ5-1-0.2-0.2 )
В05 - Welding and cutting of metals., Soldering, riveting
B51 - Non-ferrous metals, including rare metals, and their alloys


Specification :
Mechanical properties :
sв - Tensile strength , [MPa]
sT - Yield stress, [MPa]
d5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2]
HB - Brinell hardness , [MPa]

Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion (range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3]
C - Specific heat ( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]

  MNZHKT5-1-0.2-0.2   ( МНЖКТ5-1-0.2-0.2 ) - Copper-nickel alloys: chemical composition, mechanical and physical properties, hardness
Database of steels and alloys (Marochnik) contains information about chemical composition and properties more then 3000 steels and alloys