Characteristics for grade     03KH20N16АG6   ( 03Х20Н16АГ6 )



      Grade :     03KH20N16АG6   ( 03Х20Н16АГ6 )
      Classification :   Сryogenic structural steel
      Equivalent grades:     Is absent



Chemical composition in % for grade   03KH20N16АG6   ( 03Х20Н16АГ6 )
Fe C Si Mn Ni S P Cr N
50.05 - 58.85max   0.025max   0.66 - 7.515 - 16.5max   0.02max   0.02520 - 250.15 - 0.28


Mechanical properties under Т=20oС for grade   03KH20N16АG6   ( 03Х20Н16АГ6 )
Assortment Dimension Direct. sв sT d5 y KCU Heat treatment
- mm - MPa MPa % % kJ / m2 -
      780 410 52 752200Guenching 1000oC, water,


Technological properties for grade   03KH20N16АG6   ( 03Х20Н16АГ6 )
  Weldability: without limitations.




Specification :
Mechanical properties :
sв - Tensile strength , [MPa]
sT - Yield stress, [MPa]
d5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2]
HB - Brinell hardness , [MPa]

Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion (range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3]
C - Specific heat ( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]

Weldability :
without limitations - welding is done without heating and subsequent heat treeting
limited weldability - welding is possible under heating up to 100-120 grade and subsequent heat treeting
hard weldability - obtaining the quality welding needs the additional operations:heating up to 200-300 grade; the heat treeting ia annealing

  03KH20N16АG6   ( 03Х20Н16АГ6 ) - Сryogenic structural steel: chemical composition, mechanical and physical properties, hardness
Database of steels and alloys (Marochnik) contains information about chemical composition and properties more then 3000 steels and alloys