YOU HERE:   Steel and Alloy   ->   Bronze

Characteristics for grade     BrSu6F1   ( БрСу6Ф1 )



      Grade :     BrSu6F1   ( БрСу6Ф1 )
      Classification :   Tin-free foundary bronzes
      Equivalent grades:     Is absent



Chemical composition in % for grade   BrSu6F1   ( БрСу6Ф1 )
P CuSb Impurity
0.4 - 0.991.7 - 94.94.7 - 6.2 all 1.2
Comment: Cu is a basis; the percentage of Cu is given approximately.


Mechanical properties under Т=20oС for grade   BrSu6F1   ( БрСу6Ф1 )
Assortment Dimension Direct. sв sT d5 y KCU Heat treatment
- mm - MPa MPa % % kJ / m2 -
      216   5    


    Brinell hardness for     BrSu6F1   ( БрСу6Ф1 )   ,       HB 10 -1 = 78   MPa


Technological properties of the material   BrSu6F1   ( БрСу6Ф1 ) .
        Linear shrinkage : 1.3   %


Physical properties for grade   BrSu6F1   ( БрСу6Ф1 )
T E 10- 5 a 10 6 l r C R 10 9
Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m
20 0.931   46 8500    
100   17.3        




Specification :
Mechanical properties :
sв - Tensile strength , [MPa]
sT - Yield stress, [MPa]
d5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2]
HB - Brinell hardness , [MPa]

Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion (range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3]
C - Specific heat ( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]

  BrSu6F1   ( БрСу6Ф1 ) - Tin-free foundary bronzes: chemical composition, mechanical and physical properties, hardness
Database of steels and alloys (Marochnik) contains information about chemical composition and properties more then 3000 steels and alloys

    ©   2003 - 2024         Database of Steel and Alloy (russian title is the Marochnik)
Administration of the Marochnik is not responsible for the content's use.
Рейтинг@Mail.ru