| Grade : | 30KHGSА ( 30ХГСА ) |
| Substitute: | 40ХФА, 35ХМ, 40ХН, 25ХГСА, 35ХГСА |
| Classification : | Alloy structurall steel |
| Equivalent grades: | Go here |
Chemical composition in % for grade 30KHGSА ( 30ХГСА )
| C | Si | Mn | Ni | S | P | Cr | Cu |
| 0.28 - 0.34 | 0.9 - 1.2 | 0.8 - 1.1 | max 0.3 | max 0.025 | max 0.025 | 0.8 - 1.1 | max 0.3 |
Temperature of critical points for grade 30KHGSА ( 30ХГСА ).
| Ac1 = 760 , Ac3(Acm) = 830 , Ar3(Arcm) = 705 , Ar1 = 670 , Mn = 352 |
Mechanical properties under Т=20oС for grade 30KHGSА ( 30ХГСА )
| Assortment | Dimension | Direct. | sв | sT | d5 | y | KCU | Heat treatment |
| - | mm | - | MPa | MPa | % | % | kJ / m2 | - |
| Pipe, GOST 8731-87 | 686 | 11 | ||||||
| Pipe cooling strain, GOST 8733-74 | 491 | 18 | ||||||
| Bar, GOST 4543-71 | Ø 25 | 1080 | 830 | 10 | 45 | 490 | Guenching 880oC, oil, Drawing 540oC, water, | |
| Sheet trick, GOST 11269-76 | 490-740 | 20 | Normalizing | |||||
| Sheet trick, GOST 11269-76 | 1080 | 9 | 490 | Guenching and drawing | ||||
| Sheet thin, GOST 11268-76 | 490-740 | 20 | Normalizing | |||||
| Sheet thin, GOST 11268-76 | 1080 | 10 | Guenching and drawing |
| Brinell hardness for 30KHGSА ( 30ХГСА ) (annealing) , GOST 4543-71 | HB 10 -1 = 229 MPa |
| Brinell hardness for 30KHGSА ( 30ХГСА ) , Pipe GOST 8733-74 | HB 10 -1 = 229 MPa |
| Brinell hardness for 30KHGSА ( 30ХГСА ) , Bar GOST 10702-78 | HB 10 -1 = 217 MPa |
| Brinell hardness for 30KHGSА ( 30ХГСА ) (normalize) , Sheet trick GOST 11269-76 | HB 10 -1 = 156 - 217 MPa |
Technological properties for grade 30KHGSА ( 30ХГСА )
| Weldability: | limited weldability. |
| Flakes : | predisposed |
| Temper brittleness: | predisposed |
Physical properties for grade 30KHGSА ( 30ХГСА )
| T | E 10- 5 | a 10 6 | l | r | C | R 10 9 |
| Grade | MPa | 1/Grade | Watt/(m·Grade) | kg/m3 | J/(kg·Grade) | Ohm·m |
| 20 | 2.15 | 38 | 7850 | 210 | ||
| 100 | 2.11 | 11.7 | 38 | 7830 | 496 | |
| 200 | 2.03 | 12.3 | 37 | 7800 | 504 | |
| 300 | 1.96 | 12.9 | 37 | 7760 | 512 | |
| 400 | 1.84 | 13.4 | 36 | 7730 | 533 | |
| 500 | 1.73 | 13.7 | 34 | 7700 | 554 | |
| 600 | 1.64 | 14 | 33 | 7670 | 584 | |
| 700 | 1.43 | 14.3 | 31 | 622 | ||
| 800 | 1.25 | 12.9 | 30 | 693 | ||
| T | E 10- 5 | a 10 6 | l | r | C | R 10 9 |
Equivalent steels for grade 30KHGSА ( 30ХГСА )
| Bulgaria | Poland | Czechia | ||||
| BDS | PN | CSN | ||||
|
|
|
Types of delivery of grade 30KHGSА ( 30ХГСА )
| B03 - Metal forming treatment. Forgings |
| В05 - Welding and cutting of metals., Soldering, riveting |
| В22 - Graded and shaped rolling |
| B23 - Sheets and Strips |
| В32 - Graded and shaped rolling |
| B33 - Sheets and Strips |
| В62 - Steel pipes and connecting parts to them |
| В71 - Low-carbon steel wire |
Specification :
| Mechanical properties : | |
| sв | - Tensile strength , [MPa] |
| sT | - Yield stress, [MPa] |
| d5 | - Specific elongation at fracture , [ % ] |
| y | - Reduction of area , [ % ] |
| KCU | - Impact strength , [ kJ / m2] |
| HB | - Brinell hardness , [MPa] |
Physical properties : | |
| T | - Test temperature , [Grade] |
| E | - Young modulus , [MPa] |
| a | - Coefficient of linear expansion (range 20o - T ) , [1/Grade] |
| l | - Termal (heat) condition coefficient , [Watt/(m·Grade)] |
| r | - Density , [kg/m3] |
| C | - Specific heat ( range 20o - T ), [J/(kg·Grade)] |
| R | - Electrical resistance , [Ohm·m] |
Weldability : | |
| without limitations | - welding is done without heating and subsequent heat treeting |
| limited weldability | - welding is possible under heating up to 100-120 grade and subsequent heat treeting |
| hard weldability | - obtaining the quality welding needs the additional operations:heating up to 200-300 grade; the heat treeting ia annealing |
30KHGSА ( 30ХГСА ) - Alloy structurall steel: chemical composition, mechanical and physical properties, hardness
Database of steels and alloys (Marochnik) contains information about chemical composition and properties more then 3000 steels and alloys
| © 2003 - 2024 Database of Steel and Alloy (russian title is the Marochnik)
Administration of the Marochnik is not responsible for the content's use. |