| Grade : | 38KHN3MА ( 38ХН3МА ) |
| Substitute: | 38ХН3ВА |
| Classification : | Alloy structurall steel |
| Equivalent grades: | Go here |
Chemical composition in % for grade 38KHN3MА ( 38ХН3МА )
| C | Si | Mn | Ni | S | P | Cr | Mo | Cu |
| 0.33 - 0.4 | 0.17 - 0.37 | 0.25 - 0.5 | 2.75 - 3.25 | max 0.025 | max 0.025 | 0.8 - 1.2 | 0.2 - 0.3 | max 0.3 |
Temperature of critical points for grade 38KHN3MА ( 38ХН3МА ).
| Ac1 = 730 , Ac3(Acm) = 770 , Ar3(Arcm) = 315 , Ar1 = 300 |
Mechanical properties under Т=20oС for grade 38KHN3MА ( 38ХН3МА )
| Assortment | Dimension | Direct. | sв | sT | d5 | y | KCU | Heat treatment |
| - | mm | - | MPa | MPa | % | % | kJ / m2 | - |
| Bar, GOST 4543-71 | Ø 25 | 1080 | 980 | 12 | 50 | 780 | Guenching and drawing |
| Brinell hardness for 38KHN3MА ( 38ХН3МА ) (annealing) , GOST 4543-71 | HB 10 -1 = 269 MPa |
Technological properties for grade 38KHN3MА ( 38ХН3МА )
| Weldability: | is not used. |
| Flakes : | predisposed |
| Temper brittleness: | not predisposed |
Physical properties for grade 38KHN3MА ( 38ХН3МА )
| T | E 10- 5 | a 10 6 | l | r | C | R 10 9 |
| Grade | MPa | 1/Grade | Watt/(m·Grade) | kg/m3 | J/(kg·Grade) | Ohm·m |
| 20 | 2.07 | 36 | 292 | |||
| 100 | 2.03 | 11.8 | 36 | 496 | 317 | |
| 200 | 1.96 | 12.3 | 36 | 508 | 358 | |
| 300 | 1.92 | 12.7 | 35 | 525 | 425 | |
| 400 | 1.82 | 13.1 | 34 | 538 | 506 | |
| 500 | 1.73 | 13.4 | 33 | 567 | 602 | |
| 600 | 1.67 | 13.7 | 31 | 601 | 742 | |
| 700 | 1.47 | 13.9 | 30 | 672 | 890 | |
| 800 | 1.35 | 10.8 | 29 | 697 | 1100 | |
| T | E 10- 5 | a 10 6 | l | r | C | R 10 9 |
Equivalent steels for grade 38KHN3MА ( 38ХН3МА )
| Japan | |
| JIS | |
|
Types of delivery of grade 38KHN3MА ( 38ХН3МА )
| B03 - Metal forming treatment. Forgings |
| В22 - Graded and shaped rolling |
| B23 - Sheets and Strips |
| В32 - Graded and shaped rolling |
Specification :
| Mechanical properties : | |
| sв | - Tensile strength , [MPa] |
| sT | - Yield stress, [MPa] |
| d5 | - Specific elongation at fracture , [ % ] |
| y | - Reduction of area , [ % ] |
| KCU | - Impact strength , [ kJ / m2] |
| HB | - Brinell hardness , [MPa] |
Physical properties : | |
| T | - Test temperature , [Grade] |
| E | - Young modulus , [MPa] |
| a | - Coefficient of linear expansion (range 20o - T ) , [1/Grade] |
| l | - Termal (heat) condition coefficient , [Watt/(m·Grade)] |
| r | - Density , [kg/m3] |
| C | - Specific heat ( range 20o - T ), [J/(kg·Grade)] |
| R | - Electrical resistance , [Ohm·m] |
Weldability : | |
| without limitations | - welding is done without heating and subsequent heat treeting |
| limited weldability | - welding is possible under heating up to 100-120 grade and subsequent heat treeting |
| hard weldability | - obtaining the quality welding needs the additional operations:heating up to 200-300 grade; the heat treeting ia annealing |
38KHN3MА ( 38ХН3МА ) - Alloy structurall steel: chemical composition, mechanical and physical properties, hardness
Database of steels and alloys (Marochnik) contains information about chemical composition and properties more then 3000 steels and alloys
| © 2003 - 2024 Database of Steel and Alloy (russian title is the Marochnik)
Administration of the Marochnik is not responsible for the content's use. |