Characteristics for grade     30KHN3M2FА   ( 30ХН3М2ФА )

      Grade :     30KHN3M2FА   ( 30ХН3М2ФА )
      Classification :   Alloy structurall steel
      Equivalent grades:     Is absent
Grade   30KHN3M2FА   ( 30ХН3М2ФА ):   supplier   Auremo   www.auremo.biz
Sale:   Russia +7 (812) 680-16-77 ,   Germany +49 (208) 205-83-073,     info [a] auremo.org



Chemical composition in % for grade   30KHN3M2FА   ( 30ХН3М2ФА )
C Si Mn Ni S P Cr Mo V Cu
0.26 - 0.32max   0.370.2 - 0.53 - 3.5max   0.022max   0.0251.2 - 1.70.4 - 0.650.1 - 0.2max   0.25


Temperature of critical points for grade   30KHN3M2FА   ( 30ХН3М2ФА ).
Ac1 = 725 ,      Ac3(Acm) = 800


Mechanical properties under Т=20oС for grade   30KHN3M2FА   ( 30ХН3М2ФА )
Assortment Dimension Direct. sв sT d5 y KCU Heat treatment
- mm - MPa MPa % % kJ / m2 -
Forging to 500   900 750 12 35500Guenching 850 - 870oC,Drawing 580 - 650oC,


    Brinell hardness for     30KHN3M2FА   ( 30ХН3М2ФА )   (quenching, tempering) ,       HB 10 -1 = 277 - 321   MPa


Technological properties for grade   30KHN3M2FА   ( 30ХН3М2ФА )
  Weldability: hard weldability.
 Flakes : predisposed
Temper brittleness: weakly predisposed


Specification :
Mechanical properties :
sв - Tensile strength , [MPa]
sT - Yield stress, [MPa]
d5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2]
HB - Brinell hardness , [MPa]

Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion (range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3]
C - Specific heat ( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]

Weldability :
without limitations - welding is done without heating and subsequent heat treeting
limited weldability - welding is possible under heating up to 100-120 grade and subsequent heat treeting
hard weldability - obtaining the quality welding needs the additional operations:heating up to 200-300 grade; the heat treeting ia annealing

  30KHN3M2FА   ( 30ХН3М2ФА ) - Alloy structurall steel: chemical composition, mechanical and physical properties, hardness
Database of steels and alloys (Marochnik) contains information about chemical composition and properties more then 3000 steels and alloys

    ©   2003 - 2018         Database of Steel and Alloy (russian title is the Marochnik)
Administration of the Marochnik is not responsible for the content's use.
Previous address of this website was splav.kharkov.com
Рейтинг@Mail.ru