Characteristics for grade     15KhM   ( 15ХМ )

      Grade :     15KhM   ( 15ХМ )
      Classification :   Low alloy high-temperature steel
      Equivalent grades:   Go here



Chemical composition in % for grade   15KhM   ( 15ХМ )
C Si Mn Ni S P Cr Mo Cu
0.11 - 0.180.17 - 0.370.4 - 0.7max   0.3max   0.035max   0.0350.8 - 1.10.4 - 0.55max   0.3


Temperature of critical points for grade   15KhM   ( 15ХМ ).
Ac1 = 740 ,      Ac3(Acm) = 875


Mechanical properties under Т=20oС for grade   15KhM   ( 15ХМ )
Assortment Dimension Direct. sв sT d5 y KCU Heat treatment
- mm - MPa MPa % % kJ / m2 -
Pipe, GOST 8731-87     431 225 21    
Bar   longitudinal 540 350 25 672700Normalizing 900 - 920oC,Drawing 630 - 650oC, air,
Bar, GOST 4543-71 Ø 30   440 275 21 551180Guenching 880oC, air, Drawing 650oC, air,


    Brinell hardness for     15KhM   ( 15ХМ )   (annealing) ,       GOST 4543-71 HB 10 -1 = 179   MPa


Technological properties for grade   15KhM   ( 15ХМ )
  Weldability: without limitations.
 Flakes : predisposed
Temper brittleness: not predisposed


Physical properties for grade   15KhM   ( 15ХМ )
T E 10- 5 a 10 6 l r C R 10 9
Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m
20 2.05     7850    
100   12.2 44 7830 487  
200   13 41 7800    
300   13.3 41 7760    
400   13.7 39 7730    
450 1.72          
500   14 36 7700    
600   14.3 34 7660    
700   14.5        
800   13.4 29      
900   11.2 29      
1000   12.5        
T E 10- 5 a 10 6 l r C R 10 9


Equivalent steels for grade     15KhM   ( 15ХМ )
Warning! Indicated both exact and nearest equivalents.
USAGermanyJapanFranceEnglandEuropeanItalyBelgiumSpainChinaSwedenBulgariaHungaryPolandRomaniaCzechiaAustriaSouth Korea
-DIN,WNrJIS AFNORBSEN UNINBNUNEGBSSBDSMSZPNSTASCSNONORMKS
A387Gr.12Cl.2
K11562
K11564
K11572
K11597
K11757
K11789
K12062
1.7262
1.7335
1.7337
13CrMo4-4
13CrMo4-5
15CrMo5
16CrMo4-4
SCM415
SCM415H
SFVAF12
STBA20
STBA22
STFA22
STPA20
STPA22
12CD4
13CrMo4-5
14CrMo4-5
15CD3.5
15CD4.05
15CD4.5
13CrMo4-5
1501-620
1501-621
620-440
620-470
620-540
1.7335
13CrMo4-5
13CrMo4-5
14CrMo3
16CrMo3
18CrMo45KG
18CrMo45KW
A18CrMo4-5KW
B18CrMo4-5KG
14CrMo45
12CrMo4
14CrMo4-5
F.2631
12CrMo
12CrMoG
15CrMo
15CrMog
15CrMoR
2216
13CrMo4-5
14ChM
15ChM
13CrMo4-5
KL9
15HM
14CrMo4
15121
13CrMo4-4KW
SFVAF12
STHA20
STHA22


Specification :
Mechanical properties :
sв - Tensile strength , [MPa]
sT - Yield stress, [MPa]
d5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2]
HB - Brinell hardness , [MPa]

Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion (range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3]
C - Specific heat ( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]

Weldability :
without limitations - welding is done without heating and subsequent heat treeting
limited weldability - welding is possible under heating up to 100-120 grade and subsequent heat treeting
hard weldability - obtaining the quality welding needs the additional operations:heating up to 200-300 grade; the heat treeting ia annealing

  15KhM   ( 15ХМ ) - Low alloy high-temperature steel: chemical composition, mechanical and physical properties, hardness
Database of steels and alloys (Marochnik) contains information about chemical composition and properties more then 3000 steels and alloys

    ©   2003 - 2017         Database of Steel and Alloy (russian title is the Marochnik)
Administration of the Marochnik is not responsible for the content's use.
Previous address of this website was splav.kharkov.com
Рейтинг@Mail.ru