Characteristics for grade     ZlSrPdTs585-287-100   ( ЗлСрПдЦ585-287-100 )



      Grade :     ZlSrPdTs585-287-100   ( ЗлСрПдЦ585-287-100 )
      Classification :   Gold for jewellery
      Equivalent grades:     Is absent



Chemical composition in % for grade   ZlSrPdTs585-287-100   ( ЗлСрПдЦ585-287-100 )
Fe PbZn Ag OSb Bi AuPdImpurity
max   0.15max   0.0050.95 - 3.6328.2 - 29.2max   0.007max   0.005max   0.00558.5 - 599.5 - 10.5 all 0.17
Comment: Zn is a basis; the percentage of Zn is given approximately.


Technological properties of the material   ZlSrPdTs585-287-100   ( ЗлСрПдЦ585-287-100 ) .
        Melting temperature : 1150 - 1180   °C


Physical properties for grade   ZlSrPdTs585-287-100   ( ЗлСрПдЦ585-287-100 )
T E 10- 5 a 10 6 l r C R 10 9
Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m
20       14310    



Types of delivery of grade   ZlSrPdTs585-287-100   ( ЗлСрПдЦ585-287-100 )
B53 - Sheets and Strips


Specification :
Mechanical properties :
sв - Tensile strength , [MPa]
sT - Yield stress, [MPa]
d5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2]
HB - Brinell hardness , [MPa]

Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion (range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3]
C - Specific heat ( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]

  ZlSrPdTs585-287-100   ( ЗлСрПдЦ585-287-100 ) - Gold for jewellery: chemical composition, mechanical and physical properties, hardness
Database of steels and alloys (Marochnik) contains information about chemical composition and properties more then 3000 steels and alloys

    ©   2003 - 2024         Database of Steel and Alloy (russian title is the Marochnik)
Administration of the Marochnik is not responsible for the content's use.
Рейтинг@Mail.ru