| Grade : | 3KH2N2MVF ( 3Х2Н2МВФ ) |
| Classification : | Die tool steel |
| Equivalent grades: | Is absent |
| C | Si | Mn | Ni | S | P | Cr | Mo | W | V |
| 0.32 - 0.38 | 0.17 - 0.37 | 0.5 - 0.8 | 1.4 - 1.8 | max 0.03 | max 0.03 | 2 - 2.5 | 0.8 - 1 | 0.8 - 1.2 | 0.2 - 0.3 |
| Assortment | Dimension | Direct. | sв | sT | d5 | y | KCU | Heat treatment |
| - | mm | - | MPa | MPa | % | % | kJ / m2 | - |
| Forging | to 700 | tangent | 1400 | 1300 | 7 | Normalizing and drawing |
| Weldability: | hard weldability. |
| Flakes : | weakly predisposed |
| Temper brittleness: | weakly predisposed |
| Mechanical properties : | |
| sв | - Tensile strength , [MPa] |
| sT | - Yield stress, [MPa] |
| d5 | - Specific elongation at fracture , [ % ] |
| y | - Reduction of area , [ % ] |
| KCU | - Impact strength , [ kJ / m2] |
| HB | - Brinell hardness , [MPa] |
Physical properties : | |
| T | - Test temperature , [Grade] |
| E | - Young modulus , [MPa] |
| a | - Coefficient of linear expansion (range 20o - T ) , [1/Grade] |
| l | - Termal (heat) condition coefficient , [Watt/(m·Grade)] |
| r | - Density , [kg/m3] |
| C | - Specific heat ( range 20o - T ), [J/(kg·Grade)] |
| R | - Electrical resistance , [Ohm·m] |
Weldability : | |
| without limitations | - welding is done without heating and subsequent heat treeting |
| limited weldability | - welding is possible under heating up to 100-120 grade and subsequent heat treeting |
| hard weldability | - obtaining the quality welding needs the additional operations:heating up to 200-300 grade; the heat treeting ia annealing |